the cylinder rams shouldn't be case hardened, if chrome plated it can give some problems but but can be cut pretty easy with proper lathe tooling.
not really anyway to make a brass alloy harder then what it already is except to change the alloy, bearing bronze would be a better choice for the application.
not really anyway to make a brass alloy harder then what it already is except to change the alloy, bearing bronze would be a better choice for the application.