Dave, if I were in your shoes I would go with a 2.5mm electrode in something equivalent to our 6010 rods. Not too much penetration, and it is a "fast freeze" electrode which means the weld puddle solidifies quickly and helps prevent burn through. And give your material a few minutes to cool down a bit in between each bead you lay down, to prevent too much heat from building up in your parts.
But since I'm in MY shoes, I would TIG it.
Disclaimer:
I am not a professional welder, nor do I play one on TV or the interwebs. Use your own best judgement, grain of salt, etc., etc., etc.
But since I'm in MY shoes, I would TIG it.
Disclaimer:
I am not a professional welder, nor do I play one on TV or the interwebs. Use your own best judgement, grain of salt, etc., etc., etc.
Willie