No, the 'Well no' was aimed at the fact that it matters not a jot that the object to be de-rusted is all one piece, it normally would be.
It does matter however that the rust is 'in shadow' in this case as it's inside a male & female screw (if this is what the problem is - unproven as yet), and there would be very little reaction in the inter-thread parts.
It does matter however that the rust is 'in shadow' in this case as it's inside a male & female screw (if this is what the problem is - unproven as yet), and there would be very little reaction in the inter-thread parts.
Andrew Mawson, proud to be a member of MetalworkingFun Forum since Oct 2013.