thanks Ed the part had a couple of shrinks in it but it usable if I can machine it, white iron is not fun to try to cut. stuffs harder then a witches heart. I have it heat soaking in the furnace now will pull it late tonight or in the morning and see if I can get thru the skin.
I really liked it when I rolled the crucible over on its side to pour and all you see is white, thats about 2700 degrees