Cast And Plate
|
|
02-18-2014, 10:55 PM
I cast most of my own bullets and then copper plate them. It is time consuming but I find it fun.
Picture is some 308 150gr flat nose I just finished. I'm going to cast some 380 apc in the morning. Paul
Old Iron`, proud to be a member of MetalworkingFun Forum since Feb 2014.
Very nice Paul.
 Do you shoot those with or without gas checks? And what alloy(s) do you use? I do some casting too, but not as much as I used to. The only plating I do is with moly, but I normally just shoot them nekid. I would love to see your copper plating set-up.  p.s. Is that a Garand en-bloc I see hiding behind the Sweet's? 
Willie
02-19-2014, 08:47 PM
(02-19-2014, 07:29 AM)Highpower Wrote: I would love to see your copper plating set-up. Me too. I like casting bullets, or used to...Bob
Bob Wright
Metal Master Fab Salem Ohio Birthplace of the Silver and Deming drill bit. 5 Lathes, SBL Shaper, Lewis Mill, 7 drill presses, 5 welders... 
02-20-2014, 08:21 AM
OK - I have to ask - why copper plate them?
Hunting American dentists since 2015.
02-20-2014, 09:18 AM
Hello Paul,
Very interesting, how do you proceed to the copper plating? Friendships Michel
Welrod, proud to be a member of MetalworkingFun since Jun 2012.
03-02-2014, 08:59 AM
Sorry haven't been around in a while, Been busy with other things around here.
Had a little finder bender yesterday and it seem like I have a thing for preachers wifes. Only two finder benders I've had were both married to preachers and I think there the best ones to have wrecks with because there always so nice. Anyway I use zep root killer and vinegar, Heated and I'll get some pictures up as soon as I get the new pot setup my old one burned out the heater. The reason I plate is because there is know leading that way and so far I don't see any copper fouling either. And you can load them a little hotter than the plain cast bullets. I haven't used a gas check on these yet it doesn't seem like it needs it. The only problem I've ran into with cast bullets is the load won't fully cycle auto so I add about 2 Gran's of powder till I get the results I want. I mix my alloy its is a little harder than #2 but not by much. I test fired the 380 rounds Wednesday at a friends because I made them for my wifes father and I don't have a 380. They were pretty accurate for a gun with a 4 1/2" barrel. Paul
Old Iron`, proud to be a member of MetalworkingFun Forum since Feb 2014.
03-02-2014, 12:16 PM
Hello Paul,
Very happy to see you back on the post. Can I rest my question: how do you deposit the copper on the bullets? Thank you very much, Michel
Welrod, proud to be a member of MetalworkingFun since Jun 2012.
(03-02-2014, 08:59 AM)Old Iron` Wrote: ..... So, it's more of a chemical wash vs. an electrochemical plating system then?  Darren: Another reason for the coating is to cut down on air born lead vapors and particles. Some indoor ranges don't allow the use of plain lead (un-coated) bullets in order to keep the air as clean as possible, and to make cleaning out the bullet traps easier and safer for the workers. On the flip side, a local outdoor gun club here has a "cowboy" range with steel targets set up at short distances, where the only ammunition you can shoot MUST have plain lead bullets. Shooting copper jacketed bullets at close steel targets is a recipe for ricochets and injuries, as well as damaging the target plates. The ONLY exception to this rule is the use of copper washed .22LR rimfire ammunition.
Willie
03-03-2014, 07:22 AM
I use a power supply and know more than 1.5 volts, You have to check the voltage about every 15 minutes as sometimes it will go up.
I try and keep it around 1 volt, If you leave them in for to long they get spikes on them. I only leave them about 1 hour and the coating looks and feels good. I'll pickup what I need to get it running again and get some pictures. I'm changing some things on the tubing. Paul
Old Iron`, proud to be a member of MetalworkingFun Forum since Feb 2014.
03-03-2014, 08:44 PM
I got the pot up and running tonight, I only did 10 to try out the loads so here is the pictures.
#1 Pot heating up. #2 After about 15 minutes. #3 The power supply. #4 10 resized. #5 10 loaded with 6 in the gun. Hope the pictures load in the right order. Any questions just ask. I'll test them tomorrow and let you know what happened. Paul
Old Iron`, proud to be a member of MetalworkingFun Forum since Feb 2014.
|
|
« Next Oldest | Next Newest »
|